Study on Modification of Cinnamic Acid-grafted Poly(vinylidene fluoride)
Authors： DI Yujing, ZHANG Xuejun, ZHAO Jintong
Units： College of Science, North University of China
KeyWords： Poly(vinylidene fluoride); Cinnamic acid; Grafted polymer; Membrane; Hydrophilicity
ClassificationCode：TQ 028. 8
year,volume(issue):pagination： 2011, 31(1):47-50

Abstract：

Cinnamic acid (CA)-graft-poly(vinylidenefluoride) (PVDF) was synthesized using benzoyl peroxide （BPO） as initiator in a N,N-dimethylformamide (DMF) solution. FTIR spectroscopy, DSC, and TG analyses of the grafted polymers showed that the CA side chains were grafted onto the PVDF backbone. Contact angle measurements indicated that the contact angle of modified PVDF reduced from 88° to 54°. Microporous membranes were prepared from PVDF and the PVDF-g-P(CA) polymer with poly(vinyl pyrrolidone) (PVP) as the pore former by the tape
casting method. The morphology of the membranes was studied by scanning electron microscope (SEM). The membranes cast from the DMF solution of PVDF-g-P(CA) had a greater pore size distribution (600-700nm) and higher porosities than those of the pristine PVDF. The flux of the modified PVDF was 81 L/(m2•h), which increased by 16 L/(m2•h) over the pure PVDF.

Funds：
山西省高校科技研究开发项目（200611027）

AuthorIntro：
邸玉静（1984-），女，河北省石家庄市人，硕士研究生，从事高分子材料研究。

Reference：

[1] Wang D, Li K, Teo W K. Preparation and characterization of polyvinylidene fluoride (PVDF) hollow fiber membranes[J]. J Membr Sci,1999,163:211-220.
[2] Kong J, Li K. Oil removal from oil-in-water emulsions using PVDF membranes[J]. Separ Purif Technol,1999,16:83-93.
[3] 张建国,黄万抚,王世和. 膜改性在处理含油废水中的应用[J]. 城市环境与城市生态,2007,20(5):35-38.
[4] Akhtar S, Hawes C, Dudley L, et al. Coatings reduce the fouling of microfiltration membranes[J]. J Membr Sci,1995,107:209-218.
[5] 孙丽华,李星,杨艳玲,等. 浸没式超滤膜处理地表水的膜污染影响因素试验研究[J]. 给水排水,2009,35(4):18-22.
[6] Ochoa N A, Masuelli M, Marchese J. Effect of hydrophilicity on fouling of an emulsified oil wastewater with PVDF/PMMA membranes[J]. J Membr Sci,2003,226:203-211.
[7] Rahimpour A, Madaeni S S, Zereshki S, et al. Preparation and characterization of modified nano-porous PVDF membrane with high antifouling property using UV photo-grafting[J]. Appl Surf Sci,2009,255:7 455-7 461.
[8] Zhang M, Nguyen Q T, Ping Z. Hydrophilic modification of poly(vinylidene fluoride) microporous membrane[J]. J Membr Sci,2009,327:78-86.
[9] 芦艳,孟丽丽,于水利. 纳米Al2O3改性PVDF超滤膜处理含油污水研究[J]. 安全与环境学报,2008,8(4):62-64.
[10] Oshima K H, Evans-Strickfaden T T, Highsmith A K, et al. The use of a microporous polyvinylidene fluoride (PVDF) membrane filter to separate contaminating viral particles from biologically important proteins[J]. Biologicals, 1996,24(2):137-145.
[11] Wang P, Tan K L, Kang E T, et al. Plasma-induced immobilization of poly(ethylene glycol) onto poly(vinylidene fluoride) microporous membrane[J]. J Membr Sci, 2002,195:103-114.
[12] Wang Y P, Gao X H, Wang R M, et al. Effect of functionalized montmorillonite addition on the thermal properties and ionic conductivity of PVDF–PEG polymer electrolyte[J]. React Funct Polym,2008,68:1170-1177.
[13] 吉玉玲,李林繁,于洋,等. 粉体PVDF 辐射接枝苯乙烯[J]. 辐射研究与辐射工艺学 报,2009,27(2):79-83.
[14] 杨虎,许振良,周立志,等. 聚偏氟乙烯膜表面丙烯酸接枝改性研究[J]. 膜科学与技术,2006,26(4):24-31.
[15] Belfer S, Fainchtain R, Purinson Y, et al. Surface characterization by FTIR-ATR spectroscopy of polyethersulfone membranes-unmodified, modified and protein fouled[J]. J Membr Sci, 2000,172(1-2):113-124.

Service：
【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com

京公网安备11011302000819号