Study on the preparation of PTFE/CaCO3 hybrid hollow fiber membrane and the interfacial micro-voids
Authors： HUANG Qinglin, XIAO Changfa, HU Xiaoyu
Units： State Key Laboratory of Hollow Fiber Membrane Materials and Processes, Tianjin Polytechnic University, Tianjin 300160, China
KeyWords： PTFE; fiber forming; hollow fiber membrane; interfacial micro-voids.
ClassificationCode：TQ028.8
year,volume(issue):pagination： 2011, 31(6):46-49

Abstract：

Using the gel of Poly(vinyl alcohol) (PVA) and Boric acid (H3BO3) as the fiber forming polymer, introducing the nano-scale CaCO3 particles into spinning solution, Polytetrafluoroethylene(PTFE)/CaCO3 hybrid hollow fiber membrane which has the interfacial micro-voids pore structure was prepared by the concentrated PTFE suspension. The gel mechanism of PVA and H3BO3 and the effects of CaCO3 on the properties and structure of hybrid hollow fiber membrane were investigated. By the morphology observation, the hollow fiber membrane obtained was a kind of homogenous membrane. The interfacial micro-voids were different with the node-fibril network produced by biaxial stretched method. The quantity and the pore size improved with the increasing draw ratio.

Funds：
国家高技术研究发展计划（863计划）重点课题（2007AA030304），国家自然科学基金（20874073），天津市科技计划项目（10SYSYJC27900）

AuthorIntro：
黄庆林（1985-），男，江西人，博士生,研究方向：高分子膜材料。 通讯联系人：肖长发（cfxiao@tjpu.edu.cn），研究方向为功能纤维材料,联系电话：022-24528138。

Reference：

[1] WinstonHo W S, Sirkar K. K主编. Membrane Handbook[M].张志城等译.北京:海洋出版社, 1999, 424--526.
[2] Matthias Goessi, Theo Tervoort et al. Melt-spun poly(tetra?uoroethylene) ?bers[J]. J Mater Sci ,2007, 42:7983–7990.
[3] Bacino J, Gore W L, Associates Inc. USA. Thin porous PTFE film and a mamfacturing method[P]. US Pat: 5476589, 1995,12,19.
[4] Marek Gryta. Influence of Polypropylene Membrane Surface Porosity on the Performance of Membrane Distillation Process[J]. J. Membr. Sci, 2007, 287: 67-78.
[5] Yingling Liu, Chunghao Yu, Juinyih Lai. Poly(tetrafluoroethylene)/polyamide thin-film composite membranes via interfacial polymerization for pervaporation dehydration on an isopropanol aqueous solution[J]. J. Membr. Sci, 2008, 315:106-115.
[6] 陈珊妹,李敖琪.双向拉伸PTFE微孔膜的制备及其孔性能[J]. 膜科学与技术,2003, 2:19-22.
[7] 胡晓宇, 肖长发, 安树林等. PU/PVDF共混中空纤维膜结构与性能[J]. 膜科学与技术, 2007, 27,(6): 97-100.
[8] Chunsheng Feng, Rong Wang, Baoli Shi. Factors affecting pore structure and performance of poly(vinylidenefluoride-co-hexafluoro propylene) asymmetric porous membrane[J], J. Membr. Sci. 2006, 277, 55-64.
[9] 马训明, 郭玉海, 陈建勇等. 聚四氟乙烯纤维的凝胶纺丝[J]. 纺织学报, 2009, 30(3):10-12.

Service：
【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com

京公网安备11011302000819号