Characterization of Asymmetric PES/SPSF Nanofiltration membranes
Authors： Ma Feng1,2  Zhang Yu-zhong1,2  Ding Xiao-li1,2  Lin li-gang1,2  Li Hong1,2
Units： 1State Key Laboratory of Hollow Fiber Membrane Materials and Processes, Tianjin Polytechnic University, Tianjin 300106, China; 2School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300160, China
KeyWords： sulfonated polysulfone; polyethesulfone; nanofiltration; blend; asymmetric
ClassificationCode：TQ028.8
year,volume(issue):pagination： 2012, 32(1):46-50

Abstract：

 Polyethersulfone(PES)/Sulfonated polysulfone(SPSF) blend nanofiltration membranes were prepared using a simple phase inversion technique. The permeability of nanofiltration membranes fabricated with different sulfonation degree SPSF and SPSF contents was systematically studied. The results showed that nanofiltration membranes with PES/10% sulfonation degree SPSF ratio of 1.5 had high rejection of Na2SO4 (69%), NaCl(23.5%)，PEG1000(99.8%), PEG800(81%)  and，PEG600（57.8%） large pure water flux(90.3L/(m2h)) at 0.5MPa and 25℃.

Funds：
国家自然科学基金（50973083）、高等学校博士学科点专项科研基金（20091201120002），国家自然科学基金项目（50473025）。

AuthorIntro：
马冯（1985—），男，湖南常德，硕士研究生，研究生期间从事纳滤膜的研究，E-mail:zzzzmama@163.com,通讯地址：天津市河东区成林道63号天津工业大学。张玉忠，E-mail：zhangyz2004cn@163.com。

Reference：

[1] Yutaka Matsumoto. Preparation of composite UF membranes of sulfonated polysulfone coated on ceramics[J]. Journal of Membrane Science, 158 (1999) 55~62
[2] 环国兰，张宇峰，杜启云.纳滤复合膜的研制[J].水处理技术，2006.11（32）：11～14
[3] X.J.Yang,A.G.Livingstion, L.Freitas dos Santos. Experimental observations of nanofiltration with organic solvents[J]. Journal of Membrane Science, 190 (2001) 45–55
[4] 丁礼琴,刘　力,徐德生.纳滤在制药及食品中的应用进展[J].中成药,2008.8（30）：8～12
[5] Woei-Jye Lau, A.F. Ismail. Effect of SPEEK content on the morphological and electrical properties of PES/SPEEK blend nanofiltration membranes[J]. Desalination,249 (2009) 996–1005
[6] Noraaini Alia.The formation and characterisation of an asymmetric nanofiltration membrane for ammonia–nitrogen removal: Effect of shear rate[J]. Bioresource Technology, 101 (2010) 1459–1465

Service：
【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com

京公网安备11011302000819号