The preparation of environment-friendly oxygen-rich silicone rubber membrane
Authors： PENG Yuelian，AN Kun，FAN Hongwei
Units： Center of Membrane Technology, College of Environment and Energy Engineering, Beijing University of Technology, Beijing 100124, China
KeyWords： oxygen-rich; silicone rubber; latex coating; environment-friendly
ClassificationCode：TQ028.8
year,volume(issue):pagination： 2013, 33(3):54-58

Abstract：

The membrane used in air separation and oxygen enrichment is an important class of gas separation membranes. In this study, silicone rubber/polysulfone (PDMS/PS) composite membranes were prepared; the silicone rubbers included solvent-based hydroxyl silicon rubber and emulsion hydroxyl silicon rubber. The prepared composite membranes were evaluated by the permeation rate and separation factor. The results showed that the permeation rate of solvent-based silicon rubber/polysulfone membrane was 3-4 times more than that of emulsion silicon rubber/polysulfone membrane, but the latter had a little better separation factor than the former. The oxygen permeation rate Q(O2) and separation factor α (O2 N2) was 113 GPU and 2.00, respectively. This latex coating method, coating emulsion hydroxyl silicon rubber on the support, was not only environment-friendly, but also safe and economic.

Funds：
北京工业大学人才强教深化计划，创新团队项目，项目号：00500054R5004

AuthorIntro：
安坤（1985-），男，山东省德州市人，主要研究方向为膜科学与技术*通讯联系人，彭跃莲（1969—），女，湖北人，近年的主要研究方向为膜蒸馏用膜及过程，联系电话：010-67391090，Email: pyl@ bjut.edu.cn。

Reference：

[1] Stern S A. Polymers for gas separations: The next decade [J]. J Membr Sci,1994,94:1-65.
[2] 沈光林.膜法富氧技术的研究与应用[J ].现代节能,1998,14(5):4-7.
[3] Ma. Eulalia Vanegas. Syndiotactic poilpropylene copolymer membrane and their performance for oxygen separation[J ].Journal of Membrane Science,2010,348:34-40.
[4] L．Hu, X. Zhang, J. Niu, X. Wang, Structures and properties of modified ethylcellulose oxygen-enrich membranes[J ].Appl. Polym. Sci. 65 (1997) 1837-1841
[5] M. W. Hellums, W. J. Koros, G. R. Husk, D. R. Paul, Gas transport in halogen containing aromatic polycarbonates[J ]. Appl. Polym. Sci. 43(1991) 1997-1986.
[6] G. Xu, X. Sun, X. Qiu, J. Zhang, G. Zheng, XPS studies on surface modified poly[1-(trimethylsilyl)-1-propyne] membranes II surface modification by bromine vapor, Chinese J. Polym.Sci.12(1994)180-184.
[7] S.P. Nunes, K.V. Peinemann, Membrane Technology in the Chemical Industry, Second Revised and Extended Edition, Wiley-VCH, 2006.
[8] 孙余凭. 掺杂二氧化硅的硅橡胶富氧膜及其制备方法[P ].中国专利:200710131769.7,2007
-08-29.
[9] T. Aoki, Macromolecular design of permselective membranes, Prog. Polym. Sca.24 (1999) 951
[10] Zi-Yong Zhang, Hua-Xin Rao, Fan-Na Liu. Preparation and oxygen/nitrogen permeability of PDMS crosslinked membrane and PDMS / tetraethoxysilicone hybrid membrane. Journal of Membrane Science,2007,303:132-139.
[11] Zi-Yong Zhang, Facilitated oxygen transport in a novel silicone polymer membrane containing carboxylic cobalt groups, J. Appl. Polym. Sci. 90 (2003) 1038.
[12] 郭勇,华曼等.硅橡胶-聚砜中空纤维复合膜的制备及性能研究[J ].膜科学与技术,2002,22(5):58-60.
[13] P. Pandey, R. S.Chauhan, P reparation of gas separation membranes and their evaluation, Defen. Sci. [J ].54(2004)335-343
[14] 刘光仙。孙晓然. 富氧膜技术的进展[J ] 化学工程师,2006,135(12):33-37.
[15] 李宁,贺高红等.硅橡胶-聚碳酸酯富氧膜的制备[J ].膜科学与技术,2009,29(2):56-59.
[16] 李宁.基膜对硅橡胶复合膜富氧性能的影响研究[D ].大连:大连理工大学,2008.
[17] 张阳,王湛等.聚砜-硅橡胶富氧膜的制备[J ].膜科学与技术,2007,27 (3):53-56.
[18] 张志庆,徐桂英,叶繁等.十二烷基甜菜碱/十二烷基硫酸钠复配体系的表面活性[J ].物理化学学报,2001,17(12):1122-1125.

Service：
【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com

京公网安备11011302000819号