Preparation and Characterization of Cellulose acetate carbamate as Membrane materials

Authors： CHEN Fu-shan, SU Lin-hai, SONG Xiao-ming,SUN Zhong-hua

Units： College of Chemical Engineering, Qingdao University of Science and Technology, Qingdao 266042, China

KeyWords： Cellulose acetate; urea; Cellulose acetate carbamate; degree of substitution; Membrane performance

ClassificationCode：O636.1+1

year,volume(issue):pagination： 2013, 33(3):59-63

Abstract：

Using urea to cellulose acetate (CA) for soaking pretreatment, and then transfer CA into o-xylene inert system for reaction. These factors have been explored at the process of synthesis and the results were shown as follows: Pretreatment concentration was 25%, pretreatment temperature was 55 ℃, pretreatment time was 5 h, and the reaction time was 3.5 h. On this condition, the degree of substitution of CAC was able to be 0.1. FT-IR characterization proved that the CAC was successful synthetized. Use the CAC and CA for casting film, the tensile strength and water flux of CAC membrane is better than that of CA membrane. The study concluded that with the degree of substitution increases, CAC film tensile strength and water flux shows increase trend.

Funds：

国家自然科学基金项目(No.21176131).

AuthorIntro：

苏林海（1987-），男，山东淄博，主要研究方向：天然高分子的改性及应用

Reference：

[1]叶代勇, 黄洪, 傅和青等. 纤维素化学研究进展. 化工学报, 2006, 57(8): 1782-1791.
[2]Han J S, Rowell J S. Chemical Composition of Fibers in Paper and Composites from Agro-Based Resources. London: CRC Press, 1996: 832134.
[3]林卫江, 黄科林, 彭小玉等. 纤维素醋酸酯合成研究进展[J]. 企业科技与发展: 2010, 287: 4-7.
[4]Calvin Woodings. Regenerated Cellulose Fibres[M]. Cambridge: Woodhead Publishing, 2001.
[5]浙江丝绸工学院, 苏州丝绸工学院. 织物组织与织纹学(下册)[M]. 北京: 中国纺织出版社, 1997.
[6]陶美玲. 新型合成纤维醋酸纤维的生产和应用[J]. 四川化工, 2006, 9(1): 28-30.
[7]邱建华,张延武等. 表面化学法改性醋酸纤维素微滤膜[J]. 广西师范大学学报(自然科学版), 2011, 29(2): 65-70.
[8]戴清文. 聚电解质表面修饰聚丙烯微孔膜的研究[D]. 杭州: 浙江大学材料与化工学院, 2004.
[9]王宏琳,杨大令,张守海等. 分离丙烯/丙烷的超薄聚电解质中空纤维复合膜的制备[J]. 应用化学, 2007, 24( 3) : 241- 244.
[10]王渊龙. 氨基甲酸酯法绿色纤维素纤维的研究[D]. 天津: 天津工业大学, 2001: 45-50
[11]何进,梁运祥. 浅谈凯氏定氮法[J]. 陕西粮油科技,1996, 21(3): 52-53
[12]Schmidt Matthias, Peinemann Klaus-Viktor. Composite Nanofiltration Membrane[P]. EP0865309, 1998-09-23.
[13]Uragami T, Sugitani Y, Sugihara M. Studies on syntheses and permeabilities of special polymer membranes: 33. Permeation behaviour of aqueous alcohol solution through cellulose membranes, Polymer. 1982, 23: 192-196.
[14]吴金克,王彬. 超滤膜截留性能测定方法的研究[J]. 化学工程师, 2000,76: 3-5.
[15]魏国汉,戴生敏等.醋酸纤维素氨基甲酸醋的合成及其膜性能的研究[J].纤维素科学与技术,1993,1(4): 53-59.
[16]哈丽丹•买买提,努尔买买提,吾满江•艾力.纤维素氨基甲酸酯的合成[J]. 高分子材料科学与工程, 2005, 21(4): 102-104.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com