Preparation and performance of PVDF/PDA blend membranes

Authors： SHAO Bing, LIU Lifen, YANG Fenglin

Units： School of Environmental & Biological Science and Technology, Dalian University of Technology, Dalian 116023, China

KeyWords： PDA, PVDF, blend membrane, antifouling properties, hydrophilicity

ClassificationCode：TQ028.8

year,volume(issue):pagination： 2014, 34(1):57-61

Abstract：

Based on the self-polymerization of dopamine, polydopamine (PDA) was synthesized. Through addition of PDA into PVDF casting solutions, PVDF/PDA blend membranes were prepared by L-S phase inversion techniques. The morphologies and hydrophilic properties of such PVDF/PDA membranes were investigated through the methods of SEM, UF experiments, as well as antifouling tests. The effects of the blending ratio and PDA concentration on the antifouling properties of the membranes were also investigated. When the PDA concentration was 0.3%, the flux of the blend membrane was increased from 56.19 L/ (m2•h) of controlled membrane to 69.63 L/(m2•h). In order to test the antifouling performance of the membranes, the two cycle filtration test was carried out. The results showed that the antifouling properties of the blend membranes were enhanced greatly. For the first cycle and second cycle the flux recovery ratio of the PVDF/PDA membranes were both above 90%, compared with 68.5% and 56.4% of the controlled PVDF membranes.

Funds：

AuthorIntro：

邵冰（1988-），女，黑龙江人，硕士，大连理工大学环境工程专业，研究方向：MBR中的膜改性。通讯作者：柳丽芬（1965-），女，河北人，教授，博士生导师，环境工程。Email::yuzhe25521@yahoo.com.cn

Reference：

[1] Liu F, Hashim N A, Liu Y, et al. Progress in the production and modification of PVDF membranes [J]. J Membr Sci ,2011, 375: 1—27.
[2] 施柳青, 卞晓锴, 陆晓峰. 改性聚偏氟乙烯超滤膜的制备与性能的研究 [J]. 膜科学与技术,2012, 30 (6): 112—117.
[3] 邸玉静, 张学俊, 赵劲彤. 聚偏氟乙烯接枝-3-苯基丙烯酸的改性研究 [J]. 膜科学与技术,2011, 31 (1): 47—50.
[4] Xiao K B, Liu Q S, Xuan X Y, et al. Effect of Nano-TiO2 Particles on the Performance of PVDF, PVDF-g-(Maleic anhydride), and PVDF-g-Poly(acryl amide) Membranes [J]. Ind Eng Chem Res, 2011, 50: 12113–12123.
[5] Bottino A, Capannelli G, Comite A. Preparation and characterization of novel porous PVDF-ZrO2 composite membranes [J]. Desalination, 2002, 146: 35—40.
[6] Yan L, Li Y S, Xiang C B, Effect of nano-sized Al2O3 particle addition on PVDF ultra?ltration membrane performance [J]. J Membr Sci ,2006, 276 (1–2): 162–167.
[7] 张裕卿, 张红柳, 曲云. 填充纳米SiO2对聚偏氟乙烯膜性能的影响[J]. 膜科学与技术, 2007, 27(6): 47—51.
[8] Haeshin L, Dellatore S M, Miller W M, Messersmith P B, Mussel-inspired surface
chemistry for multifunctional coatings [J].Science, 2007, 318: 426–430.
[9] 徐又一, 蒋金泓, 朱利平, 朱宝库. 多巴胺的自聚-附着行为与膜表面功能化[J]. 膜科学与技术, 2011, 31(3): 32—38.
[10] Ben L, Liu W P, Jiang Z Y, Wang B Y, Zhong Y R, Ultrathin and Stable Active Layer of Dense Composite Membrane Enabled by Poly(dopamine) [J], Langmuir 2009,25(13),7368-7374.
[11] Xi Z Y, Xu Y Y, Zhu L P, Wang Y, Zhu B K. A facile method of surface modification for hydrophobic polymer membranes based on the adhesive behavior of poly(DOPA) and poly(dopamine) [J]. J Membr Sci, 2009, 327:244–253.
[12] McCloskey B D, Park H B, Ju H, Rowe B W, et al. Influence of polydopamine deposition conditions on pure water flux and foulant adhesion resistance of reverse osmosis, ultrafiltration, and microfiltration membranes [J]. Polymer, 2010, 51: 3472-3485.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com