Study on the hydrophilic modification and properties of PVDF-PET woven tubal hollow fiber composite membrane  
Authors： Zhang Ying1, Wang Lei1, Rong Zhi-yong1, Chen Li-cheng2, Wang Xu-Dong1
Units： 1. School of Environmental and Municipal Engineering, Xi’an University of Architecture & Technology,Xi’an 710055, China.
KeyWords： hydrophilization modifiers; PET woven tubal; composite membrane ；municipal secondary effluent
ClassificationCode：TQ028.8
year,volume(issue):pagination： 2014, 34(3):69-73

Abstract：

PVDF-PET woven tubal hollow fiber composite membrane were prepared using PET woven tubal for support layer, PVDF for film base material and PVA for hydrophilization modifiers in this study. The effect of the parameters of woven tube ,PVA concentration in casting solution on membrane performance and the relevant property on filter municipal secondary effluent were investigated. The test results show that when outside diameters（OD）of the PET woven tubal is increased or the mesh is decreased, the water flux and average pore diameter of composite membrane increased dramatically, while the porosity decreased. when OD was 2.1 mm mesh was 45,the water flux was 1516 L?m-2?h-1, the porosity attained 61.6%. And with the increase of PVA concentration, the water flux , average pore diameter and the porosity of composite membrane increased, meanwhile the holes in the surface of composite membrane from tiny to large. When PVA concentration was 4%，the composite membrane shown the best performance.

Funds：
国家自然科学基金项目（51278408，51178378）；陕西省教育厅专项（2013JK0884）；陕西省科技统筹创新工程计划（2012KTCL03-06）

AuthorIntro：
张颖(1987-),女,河北省唐山市，硕士研究生,研究方向为分离膜的制备与膜法水处理应用, 联系电话:18392180873, E-mail:zhangying9663@126.com

Reference：

[1] Dar-Jong Lin, Cheng-Liang Chang, et al. Preparation and characterization of microporous PVDF/PMMA composite membrane by phase inversion in water/DMSO solutions [J]. European Polymer Journal, 42(2006):2407-2418.
[2] Deshmukh S P, Li K. Effect of ethanol composition in water coagulation bath on morphology of PVDF hollow fiber membranes [J]. Journal of Membrane Science, 1998,150(1):75-85.
[3] 王磊，李薇等. 凝固浴组分对双凝固浴法制备PVDF膜结构和性能的影响[J]. 膜科学与技术，2012,32(2):5-9.
[4] 白娟莉，王磊等. 亲水化改性PVDF超滤膜的抗污染特性研究[J]. 水处理技术，2011,37(8):44-47.
[5] 吕立盈，李东亮. 聚偏氟乙烯膜的改性研究进展[J]. 化学研究，2007,18(1):103-107．
[6] 魏立超，刘振，周津. 聚偏氟乙烯纤维膜改性研究进展[J]. 化工新型材料，2008,36(10):7-9.
[7] Rong Zhiyong, Wang Lei, et al. The effect of PVDF concentration on PVDF/woven tube composite membrane and the application of composite membrane in SMBR, 2012水资源与城市发展大会,天津，2012.
[8] 吴浩赟，无纺管增强型PVDF中空纤维膜的制备研究[J].天津大学，2007,42-44
[9] 容志勇，王磊等. PVDF/编织管中空纤维复合膜的制备及其性能研究[J].水处理技术，2013.10
[10] 叶凌碧，刘大真等. 孔径为1.2µm以下的微孔膜孔径测定方法[J]. 膜分离科学与技术，1983，3(l):54-61.
[11] M. L. Yeow, K. Li. Isothermal phase diagrams and phase inversion behavior of Polymer/Solvents/Additives/Water systems [J]. Journal of Membrane Science, 2003(90): 2150-2155.
[12] 王磊，王旭东等. 水中残留有机物分子量分布特征和对膜性能的影响[J]. 水处理技术，2006,6(2):99-106.
[13] Zhang Dongxian, Sun Pengxiao, et al. Weaving Method and Mechanical Analysis of Polyethylene Terephthalate Fiber for Artificial Ligament[R]. Progress in Modern Biomdicine ,2012,12(12).

Service：
【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com

京公网安备11011302000819号