Preparation and processing parameters study of SiO2-ZrO2 composite membrane

Authors： TONG Zhi, HU Min Dun, DONG Xu Juan, ZOU Li

Units： School of Environmental and Chemical Engineering, Xi’an Polytechnic University, Xi’an 710048, China

KeyWords： sol-gel;SiO2-ZrO2 composite films; crack resistance;stability of the sol

ClassificationCode：X781.5

year,volume(issue):pagination： 2014, 34(6):35-38

Abstract：

The SiO2-ZrO2 composite membrane was prepared by sol-gel method and this paper studied the effect of sol composition and sintering process on cracking and other properties of membrane and characterized it by using ubbelohde viscometer, thermal gravimetric analysis (TG-DTG), X-ray diffraction analyzer (XRD) and atomic force microscopy (AFM). The result showed that sol composition and heating rate of sintering process in a certain temperature of the membrane played a decisive role in cracking. It can be obtained moderate viscosity, transparent and stable sol when SiO2: ZrO2 (mol / mol) = 2:0.5. The no cracking, uniform and transparent SiO2-ZrO2 composite membrane with a large surface area and narrow pore size distribution can be gotten when calcination temperature of dried gel was 600℃ at the speed of 0.5 ºC/min for 2h, meanwhile heated up slowly and insulated at 75ºC、190ºC and 230 ºC.

Funds：

陕西省教育厅基金资助项目(2013JC15)

AuthorIntro：

同帜( 1963- )，男，陕西省户县人，高级工程师，研究方向：无机陶瓷膜制备的研究与研发，

Reference：

[1] 苏毅，胡亮，刘谋盛.无机膜的特性、制造及应用[J]. 化学世界，2001,(11):604-607
[2] YOLDAS B E. Alumina gels that form porous transparent Al2O3 [J]. Journal of Membrane Science, 1975, 10: 1856−1862.
[3] 同帜, 韩丹丹, 李大川, 等. DMF对二氧化硅薄膜性能的影响[J]. 水处理技术, 2012, 38(2): 37−40.
[4] 文士美, 赵中伟. 微弧氧化法直接合成CaTi4(PO4)6生物陶瓷膜[J]. 粉末冶金材料科学与工程, 2005, 10(3): 191−194.
[5] 周健儿,吴汉阳.无机陶瓷分离膜的研究与应用—陶瓷分离膜的制备技术[J].中国陶瓷, 1999, 35(3): 16-19.
[6] J.W Chang, T.R Marrero, H.K Yasuda. Continuous process for propylene/propane separation by use of silver nitrate carrier and zirconia porous membrane[J]. Journal of Membrane Science. 2002, 205: 91-102.
[7] J.Brasseur Tilmant, C.Pommier, K.Chhor. Synthesis of supported TiO2 membranes using supercritical alcohol[J]. Materials Chemistry and Physics, 2000, 64: 156-165.
[8] 张刘忠. 分形[M]. 清华大学出版社, 1995, 182-187.
[9] 刘小林, 张伟清, 梁培辉. 水解反应温度对溶胶-凝胶SiO2增透膜光学性能的影响[J]. 光子学报, 1999, 28(6): 558.
[10] 同帜，韩丹丹,李大川，等. 甲基纤维素对SiO2薄膜性能的影响[J]. 膜科学与技术, 2013，33(1): 39-43.
[11] 同帜，韩丹丹,李大川，等. 溶剂中乙醇含量对Al2O3膜的影响[J]. 硅酸盐通报, 2012，31(1): 198-201.
[12] 向洪平，沈汝梁，邓浩强，等. TiO2溶胶稳定化制备工艺及机理研究硅[J]. 硅酸盐通报，2011，30(1) : 83-88.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com