The effect of the composite catalyst on structure and performance of the polyamide thin-film composite membrane

Authors： Wang Yuan，Wang Lei，Wang Xudong，Lv Yongtao

Units： Xi’an University of Architecture and Technology, Xi’an 710055, China

KeyWords： nanofiltration membrane；interfacial polymerization；composite catalyst；urtra-thin skin layer

ClassificationCode：TQ316.4

year,volume(issue):pagination： 2015, 35(3):1-6

Abstract：

Abstract：Polyamide thin-film composite membrane was prepared through interfacial polymerization between m-phenylenediamine (MPD) and trimesoyl chloride (TMC) on the polysulfone (PSF) support membrane. The effect of the composite catalyst (triethylamine (TEA) and camphorsulfonic acid (CSA) ), as well as the reaction conditions on the ultra-thin poly skin layer structure and performance of the nanofiltration membrane were systematically investigated. Results show that the the ultra-thin skin layer density increased, the surface roughness and the hydrophilicity contact angle decreased, and the water flux increased dramatically, while the changes to the rejection and the selecting sequence for salt of nanofiltration membrane have been very minor, as the TEA concentration in the composite catalyst increased from 0.5 wt % to 3 wt % and the molar ratio of TEA and CSA fixed at 1/2. When the concentration of TEA is 2 wt%, reaction time is 40 s, curing temperature is 80°C, curing time is 3 min，the composite nanofiltration membrane exhibited good performance that the rejection of 2 g/L MgSO4 solution was 93.2% , and the water flux was 16 L/m2h. Polyamide thin-film composite separation performance was stable at 0.2 ~ 1.0 MPa.

Funds：

国家自然科学基金项目（No.51178378; No.51278408）；陕西省科技创新（No.2012KTCL03-06;No.2013KTCL03-16）;

AuthorIntro：

西安建筑科技大学创新团队;作者简介：王元 (1989—)，女，山东济宁人，硕士研究生，主要从事聚酰胺复合纳滤膜制备研究，834956462@qq.com，18220482473；王磊（1971—），男，教授，博士生导师，主要从事水污染控制及废水再生等理论与技术的研究，通讯联系人，wl0178@126.com，西安建筑科技大学环境与市政工程学院，邮编710055

Reference：

[] Petersen R J. Composite reverse osmosis and nanofiltration membranes[J]. Journal of membrane science, 1993, 83(1): 81-150.
[]高爱环, 刘金盾, 张浩勤, 等. 聚哌嗪酰胺复合纳滤膜制备及其性能表征[J].高校化学工程学报, 2004, 18(1): 28-32.
[] Eriksson P. Nanofiltration extends the range of membrane filtration[J]. Environmental Progress, 1988, 7(1): 58-62.

[4]张烽, 徐平. 反渗透, 纳滤膜及其在水处理中的应用[J]. 膜科学与技术, 2003, 23(4): 241-245.
[]解利昕, 阮国岭, 张耀江. 反渗透海水淡化技术现状与展望[J]. 中国给水排水, 2000, 16(3): 24-27.
[] Matsumoto Y, Sudoh M, Suzuki Y. Preparation of composite UF membranes of sulfonated polysulfone coated on ceramics[J]. Journal of membrane science, 1999,
[] Zhang Y, Xiao C, Liu E, et al. Investigations on the structures and performances of a polypiperazine amide/polysulfone composite membrane[J]. Desalination, 2006, 191(1): 291-295.
[] Peng F, Huang X, Jawor A, et al. Transport, structural, and interfacial properties of poly (vinyl alcohol)–polysulfone composite nanofiltration membranes[J]. Journal of Membrane Science, 2010, 353(1): 169-176.
[]Alami-Younssi S, Larbot A, Persin M, et al. Rejection of mineral salts on a gamma alumina nanofiltration membrane Application to environmental process[J ]. Journal of membrane science, 1995, 102: 123-129.
[]谭翎燕. 新型荷电复合高脱盐纳滤膜的制备及表征[D]. 郑州大学, 2010.
[]方鹏,曹兵,淡宜,潘凯.界面聚合法制备聚酰胺纳滤膜及工艺条件对纳滤膜性能的影响[J].高分子材料与科学工程,2011,27(10):1-3.
[]Zhang W, He G H, Gao P, et al. Development and characterization of composite nanofiltration membranes and their application in concentration of antibiotics[J].Separation and Purification Technology,2003,30(9):27-35.
[]魏菊, 张守海, 武春瑞, 等. 单体结构对聚酰胺类复合膜分离性能的影响[J]. 高分子学报, 2006, 1(2): 298-302.
[]Chen G, Li S, Zhang X, et al. Novel thin-film composite membranes with improved water flux from sulfonated cardo poly (arylene ether sulfone) bearing
pendant amino groups[J]. Journal of Membrane Science, 2008, 310(1): 102-109.
[]Zhao L, Chang P C Y, Ho W S. High-flux reverse osmosis membranes incorporated with hydrophilic additives for brackish water desalination[J]. Desalination, 2013, 308: 225-232.
[]Ghosh A K, Jeong B H, Huang X, et al. Impacts of reaction and curing conditions on polyamide composite reverse osmosis membrane properties[J]. Journal of Membrane Science, 2008, 311(1): 34-45.

[]Rahimpour A, Jahanshahi M, Mortazavian N, et al. Preparation and characterization of asymmetric polyethersulfone and thin-film composite polyamide nanofiltration membranes for water softening[J]. Applied Surface Science, 2010, 256(6): 1657-1663.
[]Prakash Rao A, Desai N V, Rangarajan R. Interfacially synthesized thin film composite RO membranes for seawater desalination[J]. Journal of membrane science, 1997, 124(2): 263-272.
[]Prakash Rao A, Joshi S V, Trivedi J J, et al. Structure–performance correlation of polyamide thin film composite membranes: effect of coating conditions on film formation[J]. Journal of membrane science, 2003, 211(1): 13-24.
[]潘祖仁, 杨菁, 李姿娇, 等.高分子化学[M]. 第四版, 北京, 化学工业出版社, 2007.17~38.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com