Polyelectrolyte-TiO2 modified PVDF porous membrane and its electrochemical properties

Authors： YANG Rui1 , QIN Zhenping1, LI Mingye2, ZHAO Yao2, WANG Feng1, LI Fan1, GUO Hongxia2

Units： 1 Beijing Key Laboratory for Green Catalysis and Separation, College of Environmental and Chemical Engineering, Beijing University of Technology;

KeyWords： PVDF porous membrane; battery separators; lithium-ion conductivity; cycle performance

ClassificationCode：TB43

year,volume(issue):pagination： 2020, 40(6):51-57

Abstract：

The PVDF porous membrane was coated by the hybrid of polyelectrolyte and the modified TiO2 nanoparticles for using as lithium-ion battery separator. The variation of interface impedance, ionic conductivity and the electrochemical property of PVDF membrane before and after modification were investigated respectively. The results showed that the electrochemical performance of the modified PVDF/PDDA-TiO2 separator was obviously improved comparing with that of PVDF pristine membrane. The ionic conductivity of the PVDF/PDDA-TiO2 separator increased from 1.61×10-4 S/cm to 3.12×10-4 S/cm, while the interface impedance decreased from 114.5 Ω of the pristine PVDF separator to 96.9 Ω of the PVDF/PDDA-TiO2 separator. When the separator was assembled into lithium-ion battery, the discharged specific capacity was 75.5% after 100 cycles at 0.2C ratio.

Funds：

国家自然科学基金(21878003)，国家自然科学基金创新群体(51621003)

AuthorIntro：

杨蕊(1997-)，女，北京市人，本科生，研究方向为聚电解质功能杂化膜

Reference：

[1] Yuan M, Liu K. Rational design on separators and liquid electrolytes for safer lithium-ion batteries [J]. J. Energy Chem., 2020, 43:58-70.
[2] Kim K J, Kwon Y K, Yim T, et al. Functional separator with lower resistance toward lithium ion transport for enhancing the electrochemical performance of lithium ion batteries [J]. J. Ind. Eng. Chem. 2019, 71:228-233.
[3] Zhang K, Xiao W, Liu J, et al. A Novel Self-Binding Composite Separator Based on Poly(tetrafluoroethylene) Coating for Li-Ion Batteries [J]. Polymers, 2018, 10(12):1409 (1-13).
[4] 王健, 温乐乐, 秦德君, 等. 熔喷法制备优异热阻隔性能的锂离子电池隔膜[J]. 膜科学与技术, 2015, 35(06):33-39.
[5] Song K, Zhang P, Huang Y, et al. lectrospun PU/PVP/GO Separator for Li-ion Batteries [J]. Fiber Polym., 2019, 20(5):961-965.
[6] Kim M, Park J H. Inorganic thin layer coated porous separator with high thermal stability for safety reinforced Li-ion battery [J]. J. Power Sources, 2012, 212:22-27.
[7] Huang X, Hitt J. Lithium ion battery separators: Development and performance characterization of a composite membrane [J]. J. Membr. Sci., 2013, 425-426:163-168.
[8]武利顺, 孙俊芬, 王庆瑞. 聚偏氟乙烯膜研究进展[J]. 膜科学与技术, 2004, (05):63-68.
[9]许振良, 翟晓东, 陈桂娥. 高孔隙率聚偏氟乙烯中空纤维超滤膜的研究[J]. 膜科学与技术, 2000, (04):10-13.
[10]姜智旭, 贾金兰, 石璐, 等. L-精氨酸改性PVDF抗凝血膜的制备及血液相容性研究 [J]. 功能材料, 2015, 46(23):23109-23114.
[11]杨小进, 罗鑫, 刘东亮. 光伏组件封装用背板概述及发展趋势 [J]. 太阳能, 2017, (11):25-29.
[12] Wei W., Zhang, H. Li X., et al. Vankelecomc, Hydrophobic asymmetric ultrafiltration PVDF membranes: an alternative separator for VFB with excellent stability, Phys. Chem. Chem. Phys., 2013, 15:1766-1771
[13] Wang Y., Yin C., Song Z., et al. Application of PVDF organic particles coating on polyethylene separator for lithium ion batteries [J]. Materials, 2019, 12: 3125
[14] Min-Young A., Hee-Tak K., Duck-Rye C. Multilayered separator based on porous polyethylene layer, Al2O3 layer, and electro-spun PVDF nanofiber layer for lithium batteries [J]. J. Solid State Electrochem, 2014, 18(7):1807-1814.
[15]安亚强, 张汉鸿, 吴春丹, 等. 锂离子电池水性PVDF涂覆隔膜研究进展 [J]. 广东化工, 2019, 46(10):100-101.
[16] Costa C. M., Rodrigues H. M., Gören A., et al. Preparation of poly(vinylidene fluoride) lithium-ion battery separators and their compatibilization with ionic liquid – a green solvent approach [J]. Chem. Europe, 2017, 2(19): 5394-5402
[17] Jarvis C. R., Macklin W. J., Macklin A. J. et al. Use of grafted PVdF-based polymers in lithium batteries [J]. J. Power Sources. 2001, 97-98:664-666
[18] Li Y, Qin Z, Guo H, et al. Low-temperature synthesis of anatase TiO2 nanoparticles with tunable surface charges for enhancing photocatalytic activity[J]. PLoS One, 2014, 9, e114638:1–19.
[19] Siekierski M, Wieczorek W, Przyluski J. AC conductivity studies of composite polymeric electrolytes [J]. Electrochimica Acta, 1998, 43(10-11): 1339-1342.
[20] Raghavan P, Manuel J, Zhao X, et al. Preparation and electrochemical characterization of gel polymer electrolyte based on electrospun polyacrylonitrile nonwoven membranes for lithium batteries [J]. J. Power Sources, 2011, 196(16): 6742-6749.

Service：

【Download】【Collect】

《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone：010-80492417/010-80485372; Fax：010-80485372 ; Email：mkxyjs@163.com