碱性直接甲醇燃料电池(ADMFC)具有电极反应速率高，甲醇渗透率低的优点，阴离子交换膜是ADMFC的核心之一。论文以壳聚糖(CS)和环氧丙基三甲基氯化铵为原料合成季铵化壳聚糖，将其与聚乙烯醇(PVA)共混后制得一系列不同配比的季铵化壳聚糖(QCS)/聚乙烯醇阴离子交换膜，对膜的导电率和甲醇渗透系数进行了测试和分析。结果表明：季铵化壳聚糖与聚乙烯醇有较好的相容性，所制季铵化壳聚糖(QCS)/聚乙烯醇共混膜结构致密均匀，膜的吸水率和溶胀度随季铵化壳聚糖含量增大而减小，离子导电率随季铵化壳聚糖含量增大而提高， 80℃时季铵化壳聚糖含量为60%的共混膜导电率最高可达2.5×10-2 S/cm。膜的甲醇渗透系数低于Nafion膜。

Anion exchange membrane is the heart of alkaline direct methanol fuel cell(ADMFC). Through reaction of chitosan with (2,3-epoxypropyl) trimethylammonium chloride，quaternary ammonium groups were grafted onto the chitosan matrix successfully with high substitution degree (94.8%). A series of novel anion exchange membranes based on quaternized chitosan and poly(vinyl alcohol) blends were prepared and characterized. The morphology of the blend membranes showed that its structure was compact and uniform， which might lead to the decrease of methanol permeability. The ionic conductivity of these new anion exchange membranes rose with increasing content of quaternized chitosan. The ionic conductivity of the membrane containing 60% quaternized chitosan reached 2.5×10-2 S/cm at 80 ℃.The methanol permeability coefficients of the membranes were lower than that of Nafion 117.
Key words: quaternized chitosan; anion exchange membrane; ionic conductivity; methanol permeabiliy
 

[1] Oliveira V B, Falcao D S, Rangl C M. A comparative study of approaches to direct methanol fuel cells[J]. Int J Hydrogen Energy, 2007, 32: 415-424.
[2] 王瑾，王城，董国君，等. 碱性直接甲醇燃料电池的研究进展[J]. 电池，2007，37(4):315-317.
[3] Matsuoka K, Iriyama Y, Abe T. Alkaline direct alcohol fuel cells using an anion exchange membrane[J]. Power Sources, 2005, 150: 17-24.
[4] Varcoe J R, Slade R C T. Prospects for alkaline anion-exchange membranes in low temperature fuel cells[J].  Fuel Cells. 2005,2: 187-200.
[5] 张宏伟，刘小芬，麻小挺，等. 碱性甲醇燃料电池用季铵化PPEK膜的研究[J]. 功能材料, 2007,（3）: 412-414.
[6] Ying X, Jun F, Qing H Z, et al . Preparation and characterization of cross-linked quaternized poly(vinyl alcohol) membranes for anion exchange membrane fuel cells[J]. J Membr Sci, 2008, 311: 319-325.
[7] Wan Y, Creber K A M , Peppley B , et al. Chitosan based solid electrolyte composite membranes [J]. J Membr Sci, 2006, 280 (1-2): 666–674.
[8]崔铮，相艳，张涛. 壳聚糖固体聚合物电池用膜[J]. 化学进展， 2007,(4): 583-589.
[9]桑益洲，刘忠. 阳离子壳聚糖的合成及应用[J]. 中华纸业，2006，27(5): 45-47.
[10]伍艳辉，康峰，李佟茗. PVA-PWA-Al2O3无机—有机复合质子交换膜的研究[J]. 膜科学与技术，2007, 27(3): 57-60.
[11]张宏伟,刘小芬,麻小挺,等.碱性甲醇燃料电池用季铵化PPEK膜的研究[J]. 功能材料，2007,38（3）:412-414.                     
[12] Qin C Q, Xiao Q, Li H R, et al. Calorimetric studies of the action of chitosan-N-2-hydroxypropyl trimethyl ammonium chloride on the growth of microorganisms[J]. Biological Macromolecules，2004,34: 121-126.
[13]Xiong Y, Fang J, Zeng Q H, et al. Preparation and characterization of cross-linked quaternized poly(vinyl alcohol) membranes for anion exchange membrane fuel cells[J]. J Membr Sci, 2008, 311:319-325.
[14]Woo Y, Se Y O, Yong S K, et al. Synthesis and characterization of sulfonated polyimide membranes for direct methanol fuel cell[J]. J Membr Sci, 2003, 220(1-2): 31-45.
[15]Zhang F, Cui Z M, Li N W, et al. Synthesis of sulfonated poly(arylene-co-naphthalimide)s as novel polymers for proton exchange membranes[J]. Polymer, 2008, 49(15): 3273-3278.