以三醋酸纤维素为膜材料，以1,4-二氧六环和丙酮为溶剂，乳酸为添加剂，采用相转化法制备三醋酸纤维素正渗透膜。研究了不同支撑材料以及膜制备过程中溶剂挥发时间和添加剂的含量对正渗透膜性能的影响。结果表明，在原料液为0.1mol/L NaCl，汲取液为4mol/L葡萄糖，原料液面向分离层，室温的测试条件下，采用180目的筛网为支撑体材料，挥发时间为180秒，乳酸含量为6.6%所制备的三醋酸纤维素正渗透膜的水通量为6-7L/(m2h)，NaCl截留率在95%以上。

Cellulose triacetate forward osmosis membrane was prepared by phase inversion method. The polymer solution consisted of cellulose triacetate as the membrane material, 1, 4-dioxane and acetone as solvent, and lactic acid as additives. The effects of support materials, solvent evaporation time and the additive content on the membrane performance were investigated. 0.1mol/L NaCl was used as the feed solution and 4mol/L glucose was used as the draw solution. The water flux was between 6 and 7 L / (m2h) and the rejection for NaCl was above 95% .

[1] Holloway R W, Childress A E, Dennett K E, et al. Forward osmosis for concentration of anaerobic digester centrate [J]. Water research, 2007, 41: 4005-4014
[2] Beaudry E G, Herron J R. Direct osmosis for concentrating wastewater, Proceedings of the 27th International Conference on Environmental Systems, Lake Tahoe, July 14-17, 1997
[3] Petrotos K B, Lazarides H N. Osmotic concentration of liquid foods[J]. Food Eng., 2001,49: 201-206.
[4] Wrolstad R E, McDaniel M R, Durst R W, et al. Composition and sensory characterization of red raspberry juice concentrated by direct-osmosis or evaporation[J]. Food Sci.1993,58:633-637.
[5] Bhatt P P. Osmotic drug delivery systems for poorly soluble drugs: PharmaVentures Ltd., Oxford, UK[EB/OL].http://www.shirelabs.com/news/11 30 04.pdf,2004.
[6] Su Y C, Lin L A. Water-powered micro drug delivery system[J]. Microelectromech Syst., 2004,13: 75-82.
[7] Loeb S. Energy production at the Dead Sea by pressure-retarded osmosis: challenge or chimera[J]. Desalination, 1998, 120: 247-262.
[8] Loeb S, Hassen F V, Shahaf D. Production of energy from concentrated brines by pressure-retarded osmosis Ⅱ:experimental results and projected energy costs[J]. Membr. Sci.,1976, 1: 249-269.
[9]Cath T Y, Childress A E, Elimelech M. Forward osmosis: principles, applications, and recent developments [J]. Membr. Sci., 2006, 281:70-87.
[10] 高从堦，郑根江，汪锰等.正渗透-水纯化和脱盐的新途径[J].水处理技术,2008,34(2): 1-4.
[11] Liu L L, Wang M, Wang D, et al. Current patents of forward osmosis membrane process[J]. Recent Patents on Chemical Engineering, 2009, 2(1): 1-7.
[12] Sidney L, Leonid T, Emmanuel K, et al. Effect of porous support fabric on osmosis through a Loeb-Sourirajan type asymmetric membrane[J]. Membr. Sci. 1997, 129: 243-249.
[13] McCutcheon J R, Elimelech M. Influence of concentrative and dilutive internal concentration polarization on flux behavior in forward osmosis[J]. Membr. Sci. 2006, 284: 237–247.
[14]McCutcheon J R, Elimelech M. Influence of membrane support layer hydrophobicity on water flux in osmotically driven membrane processes[J]. Membr. Sci. 2008, 318: 458-466.
[15] 卞晓锴，陆晓峰，施柳青. 原子力显微镜及在膜科学技术研究中的应用. 膜科学与技术，2002，22(5): 36-40.
[16] 钱欣，程蓉. 原子力显微镜在合成膜表征中的应用. 膜科学与技术，2004，24(2):62-66.
[17] 张耀鹏，邵惠丽，沈新元等. 用原子力显微镜研究纤维素膜表面形貌和孔径大小的分布. 膜科学与技术，22(2): 13-16