选用来源广泛、价格低廉、可再生的芦苇作为纤维素的主要来源，以N-甲基吗啉-N-氧化物（NMMO）为溶剂，利用傅里叶红外光谱（FTIR）、X射线衍射（XRD）等着重研究了芦苇纤维素在NMMO中溶解前后结构与性能的变化，并探究了芦苇纤维素的成膜性、力学性能及耐酸耐碱性。结果发现：芦苇纤维素溶解后，聚合度较溶解前有所降低，晶型由纤维素Ⅰ变成了纤维素Ⅱ。此外，芦苇纤维素在含量为4-8%时成膜性能较好，且在浓度为8%时力学性能最好，并具有较好的耐酸耐碱性。

In this study, the reed, which is one of the most abundant and useful renewable material, was chosen as the raw material of cellulose, and its environmentally friendly regenerated cellulose membranes were successfully prepared by dissolving the reed cellulose in N-methylmorpholine-N-oxide (NMMO) solution. The structural differences between reed cellulose and cellulose regenerated from NMMO had been investigated by using Fourier transform infrared (FT-IR) spectroscopy and X-ray diffraction, and the results showed that the crystalline of reed cellulose transforms completely from celluloseⅠto celluloseⅡafter regeneration from NMMO solution. In addition, when the content of reed cellulose was between 4 and 10, the membranes presented good film-forming properties, especially, the membranes consisted of 8% reed cellulose, which not only had smooth surface, but also presented good Mechanical properties and strong acid-alkali resistance.

[1] Thomas R, Antje P, Herbert S, et a1．The chemistry of side reactions and byproduct formation in the system NMMO/cellulose (Lyocell process) [J]. Progress in Polymer Science, 2001, 26(2): 1763~1837.
[2] 张耀鹏, 邵惠丽, 沈弋弋等. 环境友好的NMMO工艺纤维素薄膜[J]. 国外纺织技术, 2000, (4): 1~4.
[3] 方红霞, 孙金余, 张雷. NMMO工艺三元绿色复合薄膜的制备和表征[J]. 高分子材料科学与工程, 2009, 25(2): 148~151.
[4] 吴翠玲, 李新平, 秦胜利等. NMMO工艺纤维素膜结构与性能的研究[J]. 包装工程, 2005, 26(2): 4~6.
[5] Chanzy H., Dube M, Marehessault RH. Crystallization of cellulose with N-methyl-morpholine-N-oxide: a new method of texturing cellulose[J].Journal of Polymer Science: Polymer Letters Edition, 1979, 17:219~226.
[6] N EL SON M L, CONNOR R T. Relation of certain infrared bands to cellulose crystallinity and crystal lattice type. PartⅠ. Spectra of lattice types, Ⅰ,Ⅱ, Ⅲ and amorphous cellulose [J]. Journal of Applied Polymer Science, 1964 (8): 1325~1341.
[7] Zhang Lina, Ruan Dong, Zhou Jinping. Structure and properties of regenerated cellulose films prepared from cotton linters in NaOH/urea aqueous solution [J]. Industrial & Engineering Chemistry Research, 2001 (40):5923~5928.