利用流变仪对聚偏氟乙烯(PVDF)/己内酰胺(CPL)热致相分离法(TIPS)成膜体系铸膜液的流变性能进行研究。考察了剪切频率、温度、PVDF质量百分含量对PVDF/CPL铸膜液体系的粘度、非牛顿性指数、粘流活化能、溶液粘弹性的影响，利用TIPS法制备PVDF膜，进一步探讨了铸膜液体系的流变性能对刮膜速率、制膜温度等成膜条件的指导作用。实验结果表明：PVDF/CPL铸膜液体系为非牛顿性流体，随着PVDF质量百分含量的升高，PVDF/CPL铸膜液体系的粘度增加，非牛顿性指数增加，粘流活化能升高，对应膜的结构越致密，水通量降低，截留率升高，膜的拉伸强度增强。PVDF质量百分含量低的铸膜液体系，制膜时对温度的灵敏度低，刮膜速率对膜的制备影响大，制膜过程需要对刮膜速率精确的控制；PVDF质量百分含量高的铸膜液体系，对温度的灵敏度高，可以在较宽的刮膜速度范围下制膜。
 

The rheology of caprolactam (CPL) solutions blends with poly (vinylidene fluoride) (PVDF) was studied by using Rheometer.The influence of different percentage PVDF content,different temperature on the PVDF/CPL casting solution system of the viscosit,the non-newtonian index,the viscous flow activation energy,modulus of solution were inspected.The PVDF microporous membranes were prepared by the method of composite thermal induced phase separation. Discuss the guiding role of the rheological  properties of casting solution system for filming conditions. The results show that PVDF/CPL casting solution system shows the characteristic of typical non-Newtonian fluid. While increasing polymer concentration, the viscosity,the non-Newtonian index and the viscous flow activation energy of polymer increased,the density of membrane and the BSA retention increased,the water flux of the membrane decreased,tensile strength of the membrane increased.The casting membrane system with low percentage PVDF content had low sensitivity to the temperature and the casting speed had a great effect on the preparation of the membrane. So the preparation of the membrane with low percentage PVDF needed precise control of the casting speed. The casting membrane system with high percentage PVDF content had high sensitivity to the temperature. The membrane with high percentage PVDF could be prepared over a wide range of casting speed at high temperature.
 

[1] Witte Pvan de. Phase separation processes in polymer solutions in relation to membrane formation [ J ].Journal of Membrane Science,1996,117 (1-2):1- 31.
[2] Z Song,M Xing,J Zhang,et al.Determination of phase diagram of a ternary PVDF/γ-BL/DOP system in TIPS process and its application in preparing hollow fiber membranes for membrane distillation[J].Separation and Purification Technology,2012.10(02):43.
[3] Fu Liu, N. Awanis Hashim, Yutie Liu et al.Progress in the production and modification of PVDF membranes [J] Journal of Membrane Science,2011,375:1-27.
[4] 谢浩军,李文刚.PVDF复合材料的流变行为研究[J]合成技术及应用,2007, 22(4) :1.
[5] Lie Shen,Yi-hu,SongYu-jian Qian et al.Rheological properties of poly(vinylidene fluoride) in molten state[J]Chinese Journal of Polymer Science Vol.26.No.5.(2008),639-644
[6] 唐振湘,孙俊芳,童发钦等.聚偏氟乙烯/聚醚酰亚胺共混溶液的流变性能研究[J]合成纤维工业,2012,35(4):1-3
[7] 张召才,郭春刚,李浩等.PVDF纺丝液流变性及其中空纤维膜纺制[J]现代塑料加工应用,2012,24(6):22-24
[8] 卢季,肖通虎,覃海娇等.稀释剂对热致相分离法制备聚偏氟乙烯膜结构的影响[J]水处理技术,2013,39(4):33-36.
[9] 任吉中,邓麦村.聚合物膜制备过程中的相关基础问题[J]膜科学与技术,2011,31(3) :39-46.
[10] Jasen J C，Macchione M，Oliviero C，et al. Rheological evaluation of the influence of polymer concentration and molar mass distribution on the formation and performance of asymmetric gas separation membranes prepared by dry phase inversion[J]．Polymer,2005,46(25)：l1366-11379．
[11] 吴其晔,巫静安.高分子材料流变学[M] 北京:高等教育出版社2002:50-72
[12]  Ferry,J.D.Viscoelastic Properties of Polymer，[M]John Wiley & Sons Inc,1980:150-160
[13] 杨庆,沈新元,郯志清等.聚丙烯腈与壳聚糖纺丝原液的流变性能研究[J] 山油化纤,2005,24（4）:15-20
[14] 金日光,华幼卿.高分子物理[M]北京: 化学工业出版社,2000:211-214
[15] 金日光.高聚物流变学及其在加工中的应用.[M]北京:化学工业出版社,1986:471-490
[16] 何曼君，陈维孝，董西侠.高分子物理[M]上海:复旦大学出版社.2001. 260-292.
[17] Lai G L, Du Z L, Li G Y. The rheological behavior of collagen dispers ion /poly( vinyla lcohol) blends [ J]. Korea -A ust Rheol J, 2007, 19( 2): 81 - 88.
[18] 李丛杰,陈蕾,刘兆峰.聚间苯二甲酰间苯二胺溶液的动态流变特性[J]东华大学学报,2007,33（1）:9-12.